Lincore® 33

Flux-Cored Self-Shielded (FCAW-S)

CLASSIFICATIONS:
EN/ISO : T Fe1

LINCORE® 33 Flux-Cored Self-Shielded Wire designed for build-up of steel mill parts such as rougher couplings, carbon steel and low alloy steel base metal build-up (Metal to Metal)

DETAILS

LINCORE® 33 ideal for rebuilding worn parts to near final dimensions before applying final hardfacing layers which are more wear resistant on tractor rolls and idlers, shovel parts, mine car wheels, mill and crusher hammers and dredge pumps applications offers unlimited layers with proper preheat and interpass temperatures and procedures.

Features

  • Delivers tough machinable deposits for build-up or final overlay intended for metal-to-metal wear
  • Use for build-up of steel mill parts such as rougher couplings
  • Build-up deposit on carbon steel and low alloy steel base metals
  • It is ideal for rebuilding worn parts to near final dimensions before applying final hardfacing layers which are more wear resistant

Typical Applications

  • Tractor rolls and idlers
  • Shovel parts
  • Mine car wheels
  • Mill and crusher hammers
  • Dredge pumps

Welding Positions

  • Flat/Horizontal

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C
Typical Result 1 Layer 14-30
Typical Result 2 Layers 26-32
Typical Result 3 Layers 25-34
Typical Result, Work-hardened 1 Layer 28-34
Typical Result, Work-hardened 2 Layers 32-36
Typical Result, Work-hardened 3 Layers 35-38
Typical Result, Flame-hardened 2 Layers 38-42

DEPOSIT COMPOSITION

Classification Product Size %Al %C %Cr %Mn %P %S %Si
Typical Result .045" (1.1 mm) 1.6-1.9 0.11-0.18 1.2-1.4 1.8-2.1 0.004-0.012 0.002-0.005 0.50-0.75
Typical Result 1/16" (1.6 mm) 1.6-1.9 0.11-0.18 1.2-1.4 1.8-2.1 0.004-0.012 0.002-0.005 0.50-0.75
Typical Result 5/64" (2.0 mm) 1.4-1.7 0.13-0.15 1.1-1.4 2.1-2.3 0.004-0.008 0.002-0.005 0.45-0.60
Typical Result 7/64" (2.8 mm) 1.4-1.7 0.13-0.15 1.1-1.4 2.1-2.3 0.004-0.008 0.002-0.005 0.45-0.60

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.)
Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 5.1 (200) 25 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 8.9 (350) 28 130 2.7 (6.0)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 12.7 (500) 31 150 3.9 (8.7)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 3.8 (150) 26 125 2.1 (4.6)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 6.4 (250) 29 180 3.5 (7.8)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 8.9 (350) 32 225 5.0 (11.1)
5/64 in (2.0 mm) DC+ 50 (2) 3.2 (125) 23 200 3.1 (6.9)
5/64 in (2.0 mm) DC+ 50 (2) 5.1 (200) 27 290 4.9 (10.8)
5/64 in (2.0 mm) DC+ 50 (2) 6.4 (250) 29 325 6.1 (21.1)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.4 (135) 26 360 5.7 (12.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 28 420 7.3 (16.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.0 (235) 30 470 9.6 (21.1)