Lincore® 102HC Metal-Cored Submerged Arc (SAW) Wire

Metal-Cored Submerged Arc (SAW) | ED026085

LINCORE® 102HC Metal-Cored Submerged Arc Wire designed for work rolls applications provides a higher hardness tool steel deposit during sliding wear (Metal to Metal)

DETAILS

LINCORE® 102HC provides higher carbon compared to LINCORE® 102W for rebuilding, deposits hot weld above 204°C (400°F) machinable offers chromium, molybdenum and tungsten chemical composition to be used with recommended Lincoln weld® 802 and Lincoln weld® 802 for semiautomatic operations.

Features

  • Metal-cored wire with a higher carbon content than Lincore® 102W
  • Will give a higher hardness tool steel deposit
  • Deposit is “hot” [above 204°C (400°F)] machinable, for easy sizing after welding

Service Information

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Flux Classification Hardness Rockwell C
Lincolnweld® 802® Typical Result 54-60

DEPOSIT COMPOSITION

Flux Classification %C %Cr %Mn %Mo %Si %V %W
Lincolnweld® 802® Typical Result 0.40 6.7 2.1 1.6 1.6 0.20 1.3

TYPICAL OPERATING PROCEDURES

Diameter Polarity Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
3/32 in (2.4 mm) DC+ 1.7 (65) 24 240
3/32 in (2.4 mm) DC+ 3.0 (120) 28 400
3/32 in (2.4 mm) DC+ 4.4 (175) 31 500
1/8 in (3.2 mm) DC+ 1.5 (60) 26 390
1/8 in (3.2 mm) DC+ 2.5 (100) 28 540
1/8 in (3.2 mm) DC+ 3.6 (140) 30 680